Product Features：
● Protects components from the risk of PID
● Superior weathering resistance (including high temperature, high humidity, UV, etc.)
● Excellent retention of adhesive properties after aging
● Excellent light transmission rate to ensure the module's power generation efficiency
● Low shrinkage to ensure stable quality during lamination
● Good operability and stability during lamination
Lamination process：
Product specification：
● Thickness: The thickness of the products we can provide is between 0.3~1.0mm, the regular thickness is 0.4~0.8mm, other thickness specifications are non-standard thickness.
● Width: maximum width 1300mm
● Length: The common specification 0.50 mm or 0.60 mm products, the length of each roll is 300m, large quantities can be customized.
Product packaging：
● Inner packing 300m/roll, inner diameter of paper tube: 76mm
● The outer packaging is special pressure-resistant carton, with dragging tray and stretch film at the bottom for fixing during transportation, 1 roll/box.
Storage and transportation：
● Store in a cool and dry room with temperature ≤ 30℃ and humidity ≤ 70%; the storage period of this product is six months from the date of production, and it is recommended to use it up within three months;
● Avoid sunlight on the film surface, avoid contact with water, grease, organic solvents and other chemicals, not exposed to air for a long time, so as not to affect its performance.
● The product should not be stacked too high for a long time, with four layers, so as not to bend and deform the product by heavy pressure.
● Avoid direct sunlight, rain, moisture and dust during transportation, prevent from heavy pressure, and take it lightly.
Precautions：
Precautions：
● Ensure that the adhesive film is stored and used in a constant temperature and humidity room.
● To avoid lamination abnormalities due to static electricity, it is recommended to remove static electricity from the entire process of the module.
● Sheeted film should be stored in a sealed container to avoid contamination and moisture, and should be used within 24 hours. -It is recommended not to use each roll near the paper tube and the outermost ring.
Lamination process：
| Lamination temperature(℃) | Evacuation time(min) | Lamination time(min) |
| 145 | 5-6 | 10-12 |
Note: According to the customer's laminating equipment, as well as the cross-linking degree requirement standard is not consistent to adjust its laminating process, subject to the actual.
Performance Parameters：
Performance Parameters：
|
Performance |
Projects |
Testing Standards |
Unit |
RP-J9001 |
|
|
Thickness |
GB/T 6672-2001 |
mm |
0.4~0.8 |
|
Tensile strength (after curing) |
GB/T 13022-91 |
Mpa |
≥8 |
|
|
Elongation at break (after curing) |
% |
≥800 |
||
|
Adhesive film and glass peel strength |
ASTM D903 |
N/cm |
≥70 |
|
|
Peel strength of adhesive film and backing plate |
N/cm |
≥40 |
||
|
Thermal Performance |
Systolicity |
ASTM 1204 |
MD% |
≤4 |
|
TD% |
≤2 |
|||
|
Cross-linking degree |
ASTM D2765 |
% |
≥75% |
|
|
Electrical performance |
Volumetric resistivity |
GB 1410-89 |
Ω.cm |
≥1.0×1015 |
|
|
Light transmittance (after curing)(280nm~380nm) |
GB/T 24102008 |
% |
≤30 |
|
Light transmittance (after curing)(380nm~1100nm) |
GB/T 2410-2008 |
% |
≥90 |
|
|
|
UV aging yellowing index |
GB/T29848 |
ΔYI |
<2.0 |
|
Humidity and heat aging yellowing index |
GB/T29848 |
ΔYI |
<4.0 |
|